- Hardness on The Spherical Surface of Steelballs
Nominal Diameter | Hardness on Spherical Surface | Nominal Diameter | Hardness on Spherical Surface | |||||
inch | mm | Rockwell "C" scale | inch | mm | Rockwell "C" scale | |||
- | 0.5 | (54-61) HRC on parellel fats, calculated from Vickers hardness observed |
29/64 | - | 60.0-65.0 | |||
- | 0.6 | 15/32 | - | |||||
- | 0.7 | - | 12 | 60.0-65.5 | ||||
1/32 | - | 31/64 | - | |||||
- | 0.8 | 1/2 | - | |||||
- | 1 | - | 13 | |||||
3/64 | - | 17/32 | - | |||||
- | 1.2 | - | 14 | |||||
- | 1.5 | 9/16 | - | |||||
1/16 | - | - | 15 | |||||
5/64 | - | 19/32 | - | |||||
- | 2 | 5/8 | - | |||||
3/32 | - | - | 16 | |||||
- | 2.5 | 21/32 | - | |||||
7/64 | - | - | 17 | 61.0-66.0 | ||||
- | 3 | 11/16 | - | |||||
1/8 | - | 54.0-59.5 | - | 18 | ||||
- | 3.5 | 54.5-60.5 | 23/32 | - | ||||
9/64 | - | - | 19 | |||||
5/32 | - | 55.5-61.5 | 3/4 | - | ||||
- | 4 | 25/32 | - | |||||
11/64 | - | 57.0-62.5 | - | 20 | ||||
- | 4.5 | 13/16 | - | |||||
3/16 | - | - | 21 | |||||
- | 5 | 57.0-62.5 | 27/32 | - | ||||
- | 5.5 | 57.5-63.0 | - | 22 | ||||
7/32 | - | 7/8 | - | |||||
- | 5.8 | - | 23 | |||||
15/64 | - | 58.0-63.5 | 29/32 | - | ||||
- | 6 | 15/16 | - | |||||
1/4 | - | - | 24 | |||||
- | 6.5 | 31/32 | - | |||||
17/64 | - | - | 25 | |||||
- | 7 | 1 | - | |||||
9/32 | - | - | 26 | |||||
- | 7.5 | 1/16 | - | |||||
19/64 | - | - | 28 | 61.0-66.5 | ||||
5/16 | - | 59.0-64.5 | 1/8 | - | ||||
- | 8 | 3/16 | - | |||||
- | 8.5 | 1/4 | - | |||||
11/32 | - | - | 32 | |||||
- | 9 | 5/16 | - | |||||
23/64 | - | - | 34 | |||||
- | 9.5 | 59.5-65.0 | 3/8 | - | ||||
3/8 | - | - | 35 | |||||
25/64 | - | - | 36 | |||||
- | 10 | 7/16 | - | |||||
13/32 | - | 60.0-65.0 | - | 38 | ||||
- | 11 | 1/2 | - | |||||
7/16 | - | 9/16 | - | |||||
- | 11.5 | - | - |